首页> 外文期刊>RSC Advances >Structure analysis of precursor alloy and diffusion during dealloying of Ag–Al alloy
【24h】

Structure analysis of precursor alloy and diffusion during dealloying of Ag–Al alloy

机译：前驱体合金的结构分析及银铝合金脱合金过程中的扩散

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nanoporous silver (NPS) was fabricated by dealloying Ag–Al alloy ribbons with nominal compositions of 30, 35 and 40 at% Ag (corresponding to hypoeutectic composition, eutectic composition and hypereutectic composition, respectively). The microstructures of the Ag–Al precursor and as-dealloyed samples were observed using a scanning electron microscope (SEM) and a transmission electron microscope (TEM) as well as via focused ion beam (FIB) technique. We concluded that with the increase in Ag content from 30 to 40 at%, the diameter of ligament increased from 70 ± 15 nm to 115 ± 35 nm. Due to the method of crystalline solidification and the distribution of α-Al(Ag) and γ-Ag _(2) Al phases, the as-dealloyed Ag _(35) Al _(65) alloy exhibited a homogeneous ligament/pore structure, whereas the microstructures of Ag _(30) Al _(70) and Ag _(40) Al _(60) showed thinner and coarser ligament structures, respectively.
机译：纳米多孔银（NPS）是通过脱银Ag-Al合金带制成的，其标称成分为30、35和40 at％Ag（分别对应于亚共晶成分，低共熔成分和过共晶成分）。使用扫描电子显微镜（SEM）和透射电子显微镜（TEM）以及通过聚焦离子束（FIB）技术观察了Ag-Al前驱体和脱合金样品的微观结构。我们得出的结论是，随着Ag含量从30 at％增加到40 at％，韧带的直径从70±15 nm增加到115±35 nm。由于采用了晶体凝固方法以及α-Al（Ag）和γ-Ag_（2）Al相的分布，因此，经过脱合金处理的Ag _（35）Al _（65）合金呈现出均匀的韧带/孔结构，而Ag _（30）Al _（70）和Ag _（40）Al _（60）的显微组织分别显示出较薄和较粗的韧带结构。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号