首页> 外文期刊>RSC Advances >A comparative study of side-chain-type poly(ether ether ketone) anion exchange membrane functionalized with different hetero-cycloaliphatic quaternary ammonium groups
【24h】

A comparative study of side-chain-type poly(ether ether ketone) anion exchange membrane functionalized with different hetero-cycloaliphatic quaternary ammonium groups

机译：不同杂环脂族季铵盐官能化的侧链型聚醚醚酮阴离子交换膜的比较研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Anion exchange membranes based on side-chain-type quarternized poly(ether ether ketone)s (QPEEKs), containing different hetero-cycloaliphatic quaternary ammonium groups, were prepared via a multi-step procedure, including polycondensation with a monomer containing pendant methylphenyl groups, bromomethylation, and followed by quaternization with 1-methylpyrrolidine (MPY), 1-methylpiperidine (MPRD), 1-methylimidazole (MIDZ) and N -methyl morpholine (MMPH), respectively. The properties of these membranes were then compared with the properties of conventional quarternized poly(ether ether ketone)s containing benzyltrimethylammonium (QPEEK-TMA). Model compounds, QMPY, QMPRD, QMIDZ and QMMPH, were synthesized and used to quantitatively compare the alkaline stability of hetero-cycloaliphatic quaternary ammonium groups using ~(1) H NMR. The results of this study indicated that the alkaline stability of all these model compounds is in the order of QMPY > QMPRD > QTMA > QMIDZ > QMMPH. These QPEEKs membranes display superior thermal, dimensional and mechanical stability. QPEEK-TMA, QPEEK-MPY and QPEEK-MPRD exhibit higher hydroxide conductivities and lower activation energies than QPEEK-MIDZ and QPEEK-MMPH. Furthermore, after exposure to 1 M NaOH at 60 °C for 24 days, QPEEK-MPY and QPEEK-MPRD demonstrated a loss in hydroxide conductivity of 28.5% and 33.4%, respectively. Both values were lower than that of QPEEK-TMA (37.7%). Therefore, among these side-chain-type QPEEKs membranes, QPEEK-MPY and QPEEK-MPRD, containing benzylmethylpyrrolidinium and benzylmethylpiperidinium as cation head-groups, are promising AEM materials for fuel cell construction.
机译：基于侧链型季铵化聚醚醚酮（QPEEKs）的阴离子交换膜，通过不同步骤制备，其中包含不同的杂环脂族季铵基团，包括与含甲基苯基侧基的单体缩聚，溴甲基化，然后分别用1-甲基吡咯烷（MPY），1-甲基哌啶（MPRD），1-甲基咪唑（MIDZ）和N-甲基吗啉（MMPH）进行季铵化。然后将这些膜的性能与传统的含苄基三甲基铵的季铵化聚醚醚酮（QPEEK-TMA）的性能进行比较。合成了模型化合物QMPY，QMPRD，QMIDZ和QMMPH，并使用〜（1）H NMR定量比较了杂环脂族季铵基团的碱性稳定性。研究结果表明，所有这些模型化合物的碱稳定性依次为QMPY> QMPRD> QTMA> QMIDZ> QMMPH。这些QPEEKs膜显示出卓越的热，尺寸和机械稳定性。与QPEEK-MIDZ和QPEEK-MMPH相比，QPEEK-TMA，QPEEK-MPY和QPEEK-MPRD具有更高的氢氧化物电导率和更低的活化能。此外，在60°C的1 M NaOH中暴露24天后，QPEEK-MPY和QPEEK-MPRD的氢氧化物电导率损失分别为28.5％和33.4％。这两个值均低于QPEEK-TMA（37.7％）。因此，在这些侧链型QPEEK膜中，含有苄基甲基吡咯烷鎓和苄基甲基哌啶鎓作为阳离子头基的QPEEK-MPY和QPEEK-MPRD是有望用于燃料电池构造的AEM材料。