首页> 外文期刊>RSC Advances >Raman spectroscopic study of ZnO/NiO nanocomposites based on spatial correlation model
【24h】

Raman spectroscopic study of ZnO/NiO nanocomposites based on spatial correlation model

机译：基于空间相关模型的ZnO / NiO纳米复合材料的拉曼光谱研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effect of nickel concentration has been investigated in ZnO/NiO nanocomposites synthesized using the co-precipitation method. The X-ray diffraction and TEM measurements confirm the distinct phase of NiO in the ZnO/NiO samples. Furthermore, the Raman study shows the sharp modes at 99 cm ~(?1) and 438 cm ~(?1) corresponding to E ~((low)) _(2) , E ~((high)) _(2) of hexagonal wurtzite ZnO structure and, 1080 cm ~(?1) associated to the two-phonon (2P) mode of NiO, respectively. We also compared the effect of Ni concentration on the formation of ZnO/NiO by analyzing E ~(high) _(2) Raman mode of ZnO with the help of spatial correlation model. The correlation lengths, broadening and asymmetry ratio obtained from the fitting showed good agreement with the experimental results.
机译：在使用共沉淀法合成的ZnO / NiO纳米复合材料中，已经研究了镍浓度的影响。 X射线衍射和TEM测量证实了ZnO / NiO样品中NiO的不同相。此外，拉曼研究显示在99 cm〜（？1）和438 cm〜（？1）处的锐模，对应于E〜（（低））_（2），E〜（（高））_（2）六方纤锌矿型ZnO的结构和1080 cm〜（？1）分别与NiO的双声子（2P）模式有关。我们还借助空间相关模型分析了ZnO的E〜（high）_（2）拉曼模式，比较了Ni浓度对ZnO / NiO形成的影响。由拟合得到的相关长度，加宽和不对称比与实验结果吻合良好。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号