首页> 外文期刊>RSC Advances >Mn4+-activated Li3Mg2SbO6 as an ultrabright fluoride-free red-emitting phosphor for warm white light-emitting diodes
【24h】

Mn4+-activated Li3Mg2SbO6 as an ultrabright fluoride-free red-emitting phosphor for warm white light-emitting diodes

机译：MN4 +活化的Li3mg2SbO6作为无氟化物的无氟红发磷，用于温暖的白色发光二极管

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this paper, we report on highly efficient Mn ~(4+) -activated double perovskite Li _(3) Mg _(2) SbO _(6) (LMS) red-emitting phosphors. These LMS:Mn ~(4+) phosphors can be efficiently excited over a broad wavelength band from 235 nm to 600 nm peaking at 344 nm and 469 nm, and exhibited an intense red emission band with a range from 600 nm to 800 nm centered around 651 nm. The optimal Mn ~(4+) doping concentration of LMS:Mn ~(4+) was 0.6 mol% and its internal quantum efficiency can reach as high as 83%. Besides, the thermal quenching effect on the optical property was also analyzed. Finally, a warm white light-emitting diode (WLED) lamp was fabricated by using a 454 nm InGaN blue LED chip combined with a blend of YAG:Ce ~(3+) yellow phosphors and the as-prepared LMS:0.6% Mn ~(4+) red phosphors, which showed bright white light with CIE chromaticity coordinates (0.4093, 0.3725), correlated color temperature (CCT = 3254 K), color rendering index (CRI = 81) and luminous efficacy (LE = 87 lm/W).
机译：在本文中，我们报告了高效的Mn〜（4+） - 活化的双钙钛矿Li _（3）Mg _（2）SBO_（6）（LMS）红发磷光体。这些LMS：Mn〜（4+）磷光体可以在335nm至600nm峰值的宽波长条带上有效激发在344nm和469nm的峰值上，并且呈现强烈的红色发射带，其范围为600nm至800nm大约651纳米。 LMS的最佳Mn〜（4+）掺杂浓度：Mn〜（4+）为0.6mol％，其内部量子效率可达高达83％。此外，还分析了对光学性质的热淬火效应。最后，通过使用454nm Ingan蓝色LED芯片与YAG的混合物结合使用温暖的白色发光二极管（WLOD）灯：Ce〜（3+）黄色磷光体和按摩为0.6％Mn〜 （4 +）红色磷光体，显示亮白光，具有CIE色度坐标（0.4093,0.3725），相关色温（CCT = 3254 k），显色指数（CRI = 81）和发光效率（Le = 87 Lm / W. ）。