首页> 外文期刊>RSC Advances >Efficient and chromaticity stable green and white organic light-emitting devices with organic–inorganic hybrid materials
【24h】

Efficient and chromaticity stable green and white organic light-emitting devices with organic–inorganic hybrid materials

机译：高效和色度稳定的绿色和白色有机发光器件，具有有机无机混合材料

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Efficient inverted bottom emissive organic light emitting diodes (IBOLEDs) with tin dioxide and/or Cd-doped SnO _(2) nanoparticles as an electron injection layer at the indium tin oxide cathode:electron transport layer interface have been fabricated. The SnO _(2) NPs promote electron injection efficiently because their conduction band (?3.6 eV) lies between the work function ( W _(f) ) of ITO (4.8 eV) and the LUMO of the electron-transporting molecule (?3.32 eV), leading to enhanced efficiency at low voltage. The 2.0% SnO _(2) NPs (25 nm) with Ir(ddsi) _(2) (acac) emissive material (SnO _(2) NPs/ITO) have an enhanced current efficiency ( η _(c) , cd A ~(?1) ) of 52.3/24.3, power efficiency ( η _(p) , lm W ~(?1) ) of 10.9/3.4, external quantum efficiency ( η _(ex) , %) of 16.4/7.5 and luminance ( L , cd m ~(?2) ) of 28?182/1982. A device with a 2.0% Cd-doped SnO _(2) layer shows higher η _(c) (60.6 cd A ~(?1) ), η _(p) (15.4 lm W ~(?1) ), η _(ex) (18.3%) and L (26?858 cd m ~(?2) ) than SnO _(2) devices or control devices. White light emission was harvested from a mixture of Cd–SnO _(2) NPs and homoleptic blue phosphor Ir(tsi) _(3) ; the combination of blue emission ( λ _(EL) = 428 nm) from Ir(tsi) _(3) and defect emission from Cd–SnO _(2) NPs ( λ _(EL) = 568 nm) gives an intense white light with CIE of (0.31, 0.30) and CCT of 6961 K. The white light emission [CIE of (0.34, 0.35) and CCT of 5188 K] from colloid hybrid electrolyte BMIMBF _(4) –SnO _(2) is also discussed.
机译：用锡氧化铟锡阴极的电子注入层和/或CD掺杂的SnO _（2）纳米粒子的高效倒置底部发光有机发光二极管（Iboleds）作为电子注入层：已经制造了电子传输层界面。 SNO _（2）NPS促进电子注入，因为它们的导电带（α3.6eV）位于ITO（4.8eV）的工作功能（W _（F））和电子传输分子的叶片之间（3.32 EV），导致在低电压下提高效率。具有IR（DDSI）_（2）（ACAC）发光材料（SNO _（2）NPS / ITO）的2.0％SNO _（2）NPS（25nm）具有增强的电流效率（η_（c），CD 52.3 / 24.3，功率效率（η_（p），lm w〜（α1））为10.9 / 3.4，外部量子效率（η_（ex），％）为16.4 / 7.5和亮度（L，Cd m〜（？2））为28？182/1982。具有2.0％CD掺杂的SnO _（2）层的装置显示出较高的η_（c）（60.6cd a〜（Δ1）），η_（p）（15.4 lm w〜（Δ1）），η _（ex）（18.3％）和l（26？858cd m〜（Δ2））而不是SnO _（2）器件或控制设备。从CD-SNO _（2）NPS和均蛋蓝磷酸二（TSI）_（3）的混合物中收获白光发射;来自IR（TSI）_（3）的蓝色发射（λ_（λ= 428nm）的组合和来自CD-SnO _（2）NPS（λ_（eL）= 568nm）的缺陷发射给出了强烈的白色CIE的光（0.31,0.30）和6961 K的CCT。来自胶体杂交电解质BMIMBF _（4）-SNO_（2）的白色光发射[CIE（0.34,0.35）和5188 k]的CCT，也是讨论。