Four color electrochromism (yellow, magenta, blue, and navy) has been achieved in Cr( III )-based metallo-supramolecular polymers ( polyCr ), which were synthesized by 1?:?1 complexation of Cr ions and 1,4-di[[2,2′:6′,2′′-terpyridin]-4′-yl]benzene (L). The polymer structure was determined by X-ray absorption fine structure (XAFS) measurement and X-ray photoelectron spectroscopy (XPS). The molecular weight of polyCr was calculated as 3.2 × 10 ~(7) Da using right angle light scattering (RALS). The EXAFS fitting indicated that the bond distances of Cr–N are 2.020 ? and 2.208 ?. A film of polyCr shows multi-color electrochromism (EC) or absorption: a sharp peak at 380 nm at 0 V vs. Ag/Ag ~(+) (yellow), a sharp peak at 510 nm and a broad peak at 800 nm at ?0.6 V vs. Ag/Ag ~(+) (magenta), a broad peak at 610 nm and between 700–900 nm at ?1.2 V vs. Ag/Ag ~(+) (blue), a broad peak between 450–900 nm at ?1.8 V vs. Ag/Ag ~(+) (navy). The transmittances change (Δ T ), the switching times for coloring and bleaching ( T _(c) , T _(b) ) and the coloration efficiency ( η _(c) , η _(b) ): [Δ T , ( T _(c) , T _(b) ), ( η _(c) , η _(b) )] were [39.2%, (5.56 s, 1.39 s), (169 cm ~(2) C ~(?1) , 230 cm ~(2) C ~(?1) )] at 510 nm between ?0.6 and 0.2 V vs. Ag/Ag ~(+) , [67.0%, (6.93 s, 2.52 s), (138 cm ~(2) C ~(?1) , 172 cm ~(2) C ~(?1) )] at 610 nm between ?1.2 and 0.2 V vs. Ag/Ag ~(+) , [86.1%, (6.80 s, 3.03 s), (167 cm ~(2) C ~(?1) , 134 cm ~(2) C ~(?1) )] at 780 nm between ?1.8 and 0.2 V vs. Ag/Ag ~(+) , respectively, during the cycles. The durability experiment indicates that polyCr shows an EC property for at least 100 cycles.
机译：在Cr（III）的金属 - 超分子聚合物（Polycr）中已经实现了四种彩色电致变色（黄色，品红色，蓝色和海军），该聚合物（Polycr）被1×1〜1的络合和1,4-DI合成[2,2'：6'，2'' - Terpyridin] -4'-Y1]苯（1）。通过X射线吸收细结构（XAF）测量和X射线光电子谱（XPS）测定聚合物结构。使用直角光散射（RALS）计算PolyCR的分子量为3.2×10〜（7）Da。 exafs拟合表明cr-n的键距离为2.020？和2.208？。多彩电致变色（EC）或吸收：在0V与Ag / Ag〜（+）（黄色）的380nm处，在510nm处的尖峰和800nm的尖峰峰值在α0.6V与Ag / Ag〜（+）（+）（洋红色），610nm处的宽峰，在700-900nm之间，在Δ1.2V与Ag / Ag〜（+）（蓝色）之间，之间的宽峰450-900 nm at？1.8 V与AG / AG〜（+）（海军）。透射率改变（ΔT），用于着色和漂白的切换时间（t _（c），t _（b））和着色效率（η_（c），η_（b））：[Δt， （t _（c），t _（b）），（η_（c），η_（b））] [39.2％，（5.56 s，1.39 s），（169厘米〜（2）c〜 （α1），230cm〜（2）C〜（α1））]在510nm之间，在α0.6和0.2V与Ag / Ag〜（+）之间，[67.0％，（6.93 s，2.52 s）， （138厘米〜（2）C〜（α1），172cm〜（2）C〜（α1））在Δ1.2和0.2V与Ag / Ag〜（+）之间以610nm，[86.1％] ，（6.80 s，3.03 s），（167厘米〜（2）c〜（？1），134cm〜（2）c〜（Δ1））]在780nm之间，在Δ1.8和0.2 V与AG /分别在循环期间分别为Ag〜（+）。耐久性实验表明Polycr显示4个额外的EC属性。