摘要

In this work, Ni-MOF (R-160) with a hierarchical flower-like structure is fabricated by a facile solvothermal method with surfactant assistance. Benefiting from its structure, R-160 has a very high specific surface area and a large number of exposed active sites. Electrochemical research results show that the electrochemical performance of R-160 prepared with sodium dodecyl sulfate (SDS) is superior to that of B-160 prepared without SDS assistance. For instance, the specific capacitance of B-160 is only 808 F g-1 at a current density of 1 A g-1. Nevertheless, the specific capacitance of R-160 reaches 1036 Fg-1 under the same conditions, which is 28.2% higher than that of B-160. Moreover, the energy density of an asymmetric device assembled with R-160 and AC is 38.3 W h kg-1 at a power density of 749.9 Wkg-1.
机译：在这项工作中，具有等级花状结构的Ni-Mof（R-160）通过具有表面活性剂辅助的容易溶剂的方法制造。 从其结构中受益，R-160具有非常高的比表面积和大量暴露的活性位点。 电化学研究结果表明，用十二烷基硫酸钠（SDS）制备的R-160的电化学性能优于在没有SDS辅助的情况下制备的B-160的电化学性能。 例如，B-160的特定电容在电流密度为1A G-1的情况下仅为808F G-1。 然而，R-160的比电容在相同条件下达到1036fg-1，比B-160的28.2％高28.2％。 此外，用R-160和Ac组装的不对称装置的能量密度为38.3WH kg-1，功率密度为749.9WKG-1。