首页> 外文期刊>International Journal of Electrochemical Science >N/O Co-doped Hollow Carbon Nanocapsules-Supported Ge Nanoparticles as Anodes for Excellent Performance Lithium-ion batteries
【24h】

N/O Co-doped Hollow Carbon Nanocapsules-Supported Ge Nanoparticles as Anodes for Excellent Performance Lithium-ion batteries

机译：N / O共掺杂中空碳纳米胶囊 - 支撑的GE纳米粒子作为优异的锂离子电池的阳极

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this work, a novel N/O Co-doped hollow carbon nanocapsule-supported Ge nanoparticles nanocomposite (Ge-N/O-CNCs) was successfully prepared by a facile heating reflux method. N/O codoped hollow carbon nanocapsule-supported Ge nanoparticles not only relieve the agglomeration of Ge nanoparticles and control the volume expansion, but also facilitate the rapid transmission of electrons. In LIBs, the unique Ge-N/O-CNCs nanoarchitecture was used as the anode material. At a high current density of 1 A g-1 , it remains a stable specific capacity of 448 mAh g-1 remained after 100 cycles. Additionally, even at 3.2 A g-1 , this material exhibited a high-rate specific capacity of 350 mAh g-1.
机译：在这项工作中，通过容易加热回流方法成功地制备了一种新型N / O共掺杂中空碳纳米胶囊的GE纳米颗粒纳米复合材料（GE-N / O-CNCS）。 N / O编号中空碳纳米腐蛋白载体的GE纳米颗粒不仅释放GE纳米颗粒的附聚并控制体积膨胀，还促进了电子的快速传递。 在LIBS中，使用独特的GE-N / O-CNCS纳米建筑用作阳极材料。 在高电流密度为1Ag-1，它仍然是在100次循环之后仍然存在448mAhg-1的稳定特定容量。 此外，即使在3.2AG-1中，该材料也表现出350mAhg-1的高速特异性容量。