首页> 外文期刊>Fire and materials >PIPD, A New High-modulus and High-strength Polymer Fibre with Exceptional Fire Protection Properties
【24h】

PIPD, A New High-modulus and High-strength Polymer Fibre with Exceptional Fire Protection Properties

机译：PIPD，一种具有出色防火性能的新型高模量和高强度聚合物纤维

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The development of the new high-modulus and high-strength fibre M5, made of poly{2,6-diimidazo[4,5-b:4',5'-e]-pyridinylene-1,4(2,5-dihydroxy)phenylene} or PIPD, has resulted in an organic polymer fibre with exceptional fire protection properties when compared with PBO, Twaron, Kevlar and Nomex fibres. The PIPD as-spun fibre with a modulus of 150 GPa and a tensile strength of 2.5 GPa is a crystal hydrate containing 21 wt% water. Cone calorimeter measurements yielded a fire performance index (FP1) 20 times higher than Nomex, with extremely low value for the specific extinction area (SEA) characterizing the smoke formation. The PIPD-HT fibre (recrystallized in an after treatment into the anhydrous crystalline structure) with a modulus > 300 GPa and a strength > 5 GPa has a FPI value similar to PBO but shows much less smoke formation than this fibre.
机译：由聚{2,6-二咪唑并[4,5-b：4'，5'-e]-吡啶亚基-1,4（2,5-）制成的新型高模量高强度纤维M5的开发与PBO，Twaron，Kevlar和Nomex纤维相比，二羟基二苯醚或PIPD产生了具有出色防火性能的有机聚合物纤维。 PIPD初纺纤维的模量为150 GPa，拉伸强度为2.5 GPa，是一种含有21 wt％水的晶体水合物。锥形量热仪的测量得出的防火性能指数（FP1）是Nomex的20倍，其特定消光区域（SEA）的值极低，可表征烟雾的形成。具有大于300 GPa的模量和大于5 GPa的强度的PIPD-HT纤维（在后处理中重结晶为无水晶体结构）的FPI值类似于PBO，但与该纤维相比，烟气的形成少得多。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号