首页> 外文期刊>IEEE Transactions on Magnetics >Magnetic properties of (Fe,Co)-B-Al-Nb alloys with ultrafine grain structure
【24h】

Magnetic properties of (Fe,Co)-B-Al-Nb alloys with ultrafine grain structure

机译：具有超细晶粒结构的（Fe，Co）-B-Al-Nb合金的磁性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The magnetic properties of (Fe,Co)-B-Al-Nb alloys prepared by rapid solidification process have been studied for the development of a new type Fe-based nanocrystalline alloy. Microstructure composed of ultrafine bcc Fe(Co) has been obtained directly from the rapid solidification by adding 10 at.% Al to (Fe/sub 0.85/Co/sub 0.15/)/sub 80/B/sub 20/ alloy. Furthermore, the addition of 2/spl sim/6 at% Nb to (Fe/sub 0.85/Co/sub 0.15/)/sub 70/B/sub 20/Al/sub 10/ alloy decreases the saturation magnetostriction below 5 ppm. Heat treatment of as-prepared alloys further improves its soft magnetic properties in high frequency range. (Fe/sub 0.85/Co/sub 0.15/)/sub 70/B/sub 18/Al/sub 10/Nb/sub 2/ alloy annealed at 400/spl deg/C for 1 h shows the microstructure composed of ultrafine grains of about 8 nm and the most improved magnetic properties among the prepared alloys.
机译：为了开发新型的铁基纳米晶合金，已经研究了通过快速凝固工艺制备的（Fe，Co）-B-Al-Nb合金的磁性。通过向（Fe / sub 0.85 / Co / sub 0.15 /）/ sub 80 / B / sub 20 /合金中添加10 at。％Al可以直接从快速凝固中直接获得由超细bcc Fe（Co）组成的组织。此外，向（Fe / sub 0.85 / Co / sub 0.15 /）/ sub 70 / B / sub 20 / Al / sub 10 /合金中添加2 / spl sim / 6 at％Nb将饱和磁致伸缩率降低到5 ppm以下。所制备合金的热处理在高频范围内进一步改善了其软磁性能。 （Fe / sub 0.85 / Co / sub 0.15 /）/ sub 70 / B / sub 18 / Al / sub 10 / Nb / sub 2 /在400 / spl deg / C退火1 h的合金显示了由超细晶粒组成的显微组织在约8nm的波长范围内，并且在所制备的合金中磁性能最改善。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号