To clarify the mechanism of CaS formation on the oxide inclusion of the CaO-Al_2O_3 system, the sulfide capacities of solid oxides was measured in the present study. The results show that the sulfide capacity of (12CaO·7Al_2O_3; C_(12)A_7) was much larger than of other compounds, and increased with temperature. The value for C_(12)A_7 was larger than that measured for the liquid oxide of the same composition. Furthermore, the diffusion behavior of sulfur in solid steel to the inclusion of the CaO-Al_2O_3 system, was investigated using a diffusion couple. After heating at 1 473 K for 72 h, in the case of C_(12)A_7, the intensity of sulfur in the oxide was high, but the formation of CaS was not detected. This suggests that the formation of CaS was suppressed around the C_(12)A_7 particles by the diffusion of sulfur in the solid oxide.
机译：为了阐明CAS形成对CaO-Al_2O_3系统的氧化物的机理，在本研究中测量固体氧化物的硫化物能力。结果表明（12CaO·7AL_2O_3; C_（12）A_7）的硫化物容量大于其他化合物，并随温度的增加而增加。 C_（12）A_7的值大于相同组成的液体氧化物的值。此外，使用扩散耦合研究了固体钢中固体钢中的硫的扩散行为，以包含CaO-Al_2O_3系统。在加热后，在1 473K持续72小时后，在C_（12）A_7的情况下，氧化物中硫的强度高，但未检测到CAS的形成。这表明通过在固体氧化物中的硫的扩散来抑制CAS（12）A_7颗粒的形成。

著录项

  • 来源
    《ISIJ international》 |2020年第8期|1617-1623|共7页
  • 作者

    Yosuke BABA; Xu GAO; Shigeru UEDA; Shin-ya KITAMURA;

  • 作者单位

    Graduate School of Engineering Tohoku University. Now at Materials Engineering Department Customer Performance and CAE/Test Engineering Division Nissan Motor Co. Ltd. 560-2 Okatsukoku Atsugi Kanagawa 243-0192 Japan;

    Institute of Multidisciplinary Research for Advanced Materials Tohoku University 2-1-1 Katahira Aoba-ku Sendai Miyagi 980-8577 Japan;

    Institute of Multidisciplinary Research for Advanced Materials Tohoku University 2-1-1 Katahira Aoba-ku Sendai Miyagi 980-8577 Japan;

    Institute of Multidisciplinary Research for Advanced Materials Tohoku University 2-1-1 Katahira Aoba-ku Sendai Miyagi 980-8577 Japan;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

    inclusion; CaS; Calcium-Aluminate; sulfide capacity; diffusion couple;

    机译：纳入;CAS;钙铝酸盐;硫化物容量;扩散夫妇;

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号