首页> 外文期刊>ISIJ international >Texture and Planar Anisotropy in Lean Duplex Stainless Steel Sheet
【24h】

Texture and Planar Anisotropy in Lean Duplex Stainless Steel Sheet

机译：贫双相不锈钢薄板的织构和平面各向异性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The comparison of texture and planar anisotropy of the r-value between the lean Type 32101 (21.2%Cr-1.5%Ni-5.0%Mn-0.3%Mo-0.02%C-0.22%N) and standard Type 329J4L (25.2%Cr-6.9%Ni-0.7%Mn-3.0%Mo-0.02%C-0.11%N) duplex stainless steel cold-rolled and annealed sheets were examined. Type 32101 had a weaker texture, especially in the α phase, and a lower planar anisotropy of the r-value compared with Type 329J4L. These differences were caused by the cold rolling texture because the α_(bcc) fiber (<011>// RD) texture in Type 32101 decreased during cold rolling. It was revealed that during cold rolling, inhomo-geneous deformation easily occurred in Type 32101 because this steel contained a higher volume fraction of the γ phase harder than the α phase.
机译：贫32101型（21.2％Cr-1.5％Ni-5.0％Mn-0.3％Mo-0.02％C-0.22％N）和标准329J4L型（25.2％Cr）的r值的织构和平面各向异性的比较对-6.9％Ni-0.7％Mn-3.0％Mo-0.02％C-0.11％N）双相不锈钢进行了冷轧和退火处理。与329J4L型相比，32101型具有较弱的织构，尤其是在α相中，r值的平面各向异性较低。这些差异是由于冷轧织构引起的，因为32101型的α_（bcc）纤维（<011> // RD）织构在冷轧过程中降低了。结果表明，在冷轧过程中，32101型很容易发生不均匀变形，因为这种钢所含的γ相体积分数比α相硬得多。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号