摘要

The activity coefficient of silicon in the molten Fe-C-B-Si alloy was determined by conducting the following measurements: 1) Equilibrium contents of boron in the Fe-B-Si-N alloys saturated with solid BN under Ar + N_2 gas mixture at 1 723 K, 2) Solubility of carbon in the molten Fe-C-B-Si alloy at 1 573 and 1 723 K, and 3) Equilibrium distribution of silicon between the molten Fe-C-B-Si alloy and molten stiver at 1 723 K. By using the interstitial solution model, the activity coefficient and the interaction parameters of silicon in the Fe-C-B-Si alloy were determined to be: θ_B~(Si) = 7.54 (y_(Si) < 0.15, 1 723 K), In ψ_(Si)~O = -8.7, θ_(Si)~(Si) = 18.4 (y_(Si) < 0.2, 1 723 K), θ_C~(Si) = 297 000/T -2.63 (y_(Si) < 0.4, 1 573-1 873 K)
机译：通过进行以下测量确定熔融的Fe-CB-Si合金中硅的活度系数：1）在Ar + N_2混合气体下于1的固态BN饱和的Fe-B-Si-N合金中硼的平衡含量723 K，2）碳在熔融Fe-CB-Si合金中的溶解度为1 573和1 723 K，3）硅在熔融Fe-CB-Si合金和熔融钎料之间的平衡分布在1723K。使用间隙溶液模型，确定Fe-CB-Si合金中硅的活度系数和相互作用参数为：θ_B〜（Si）= 7.54（y_（Si）<0.15，1723 K），Inψ_ （Si）〜O = -8.7，θ_（Si）〜（Si）= 18.4（y_（Si）<0.2，1723 K），θ_C〜（Si）= 297 000 / T -2.63（y_（Si）< 0.4，1 573-1 873 K）

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号