首页> 外文期刊>Journal of Applied Physics >Screen-printed multicrystalline silicon solar cells with porous silicon antireflective layer formed by electrochemical etching
【24h】

Screen-printed multicrystalline silicon solar cells with porous silicon antireflective layer formed by electrochemical etching

机译：具有通过电化学蚀刻形成的多孔硅抗反射层的丝网印刷多晶硅太阳能电池

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The latest results on the use of porous silicon (PS) as an antireflection coating (ARC) in simplified processing for multicrystalline silicon (mc-Si) solar cells are presented. A PS layer with optimal antireflection characteristics was obtained for charge density (Q) of 5.2 C/cm~2. The weighted reflectance was reduced to 4.7% in the range of wavelengths between 400 and 1000 nm. Also, the optimization of a PS selective emitter formation results in a 13.2% efficiency mc-Si cell (2 X 2 cm~2) with the electroplating method. Specific attention is given to the implementation of a PS ARC into a commercially compatible screen-printed solar cell process.
机译：提出了在简化多晶硅（mc-Si）太阳能电池加工中使用多孔硅（PS）作为减反射涂层（ARC）的最新结果。获得具有最佳抗反射特性的PS层，其电荷密度（Q）为5.2 C / cm〜2。在400和1000 nm之间的波长范围内，加权反射率降低到4.7％。同样，通过电镀方法优化PS选择性发射极的形成可以使效率为13.2％的mc-Si电池（2 X 2 cm〜2）。特别注意将PS ARC实施到商业兼容的丝网印刷太阳能电池工艺中。

著录项

  • 来源
    《Journal of Applied Physics》 |2007年第10期|p.104515.1-104515.4|共4页
  • 作者

    Jae-Hong Kwon; Soo-Hong Lee; Byeong-Kwon Ju;

  • 作者单位

    Display and Nanosystem Laboratory, College of Engineering, Korea University, Anam-dong, Seongbuk-gu, Seoul 136-701, Republic of Korea;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 应用物理学;计量学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号