首页> 外文期刊>Journal of Applied Physics >Metallic conductivity and air stability in copper chloride intercalated carbon fibers
【24h】

Metallic conductivity and air stability in copper chloride intercalated carbon fibers

机译：氯化铜插层碳纤维的金属导电性和空气稳定性

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We have formed carbon‐copper chloride intercalation compounds using variously graphitized carbon fibers as host materials. The resultant conductors are air stable, thermally stable to 450 °K, have electrical resistivities as low as 12.9 μ Ω cm at room temperature, and have metallic conductivity temperature dependencies. These intercalated fibers have tensile strengths of 160 000 psi, and Young’s moduli of 25×106 psi. For aerospace use, (resistivity×density)-1 is a figure of merit. On this basis, a reduction in resistivity by a factor of two will make this conductor competitive with copper.
机译：我们使用各种石墨化碳纤维作为基质材料形成了碳-铜氯化物插层化合物。所得导体是空气稳定的，热稳定至450°K，在室温下的电阻率低至12.9μΩΩ·cm，并且具有金属导电性温度依赖性。这些插层纤维的抗拉强度为160 000 psi，杨氏模量为25×106 psi。对于航空航天应用，（电阻率×密度）-1是一个品质因数。在此基础上，将电阻率降低两倍，可以使该导体与铜竞争。

著录项

  • 来源
    《Journal of Applied Physics》 |1982年第12期|P.9220-9223|共4页
  • 作者

  • 作者单位
  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种
  • 中图分类
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号