首页> 外文期刊>Journal of Applied Physics >Heat‐treatment studies on thin‐film CdS/CuxS solar cells
【24h】

Heat‐treatment studies on thin‐film CdS/CuxS solar cells

机译：薄膜CdS / CuxS太阳能电池的热处理研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effects of hydrogen heat treatments are reported on CdS/CuxS polycrystalline thin‐film solar cells. The short‐circuit current Isc of the cells changes in an exponential manner such that Isc =Isc (t=0)e(t/τ)1/2. The principle physical mechanism responsible for this change appears to be copper diffusion through the CuxS layer as copper oxides at the surface are reduced or formed. We were able to maximize the cell efficiency with an error of 5% or less by monitoring changes in cell parameters during heat treatments. Changes in CuxS stoichiometry were correlated with the sheet resistance of the CuxS layer in completed cells. Results indicate that heat treatment in a hydrogen atmosphere causes an increase in resistivity (corresponding to an increase in stoichiometry) while oxygen causes the reverse.
机译：氢热处理对CdS / CuxS多晶薄膜太阳能电池的影响已有报道。电池的短路电流Isc呈指数变化，使得Isc = Isc（t = 0）e（t /τ）1/2。造成这种变化的主要物理机制似乎是铜在CuxS层中的扩散，因为表面上的氧化铜被还原或形成。通过监控热处理过程中电池参数的变化，我们能够以5％或更小的误差最大化电池效率。 CuxS化学计量的变化与完成电池中CuxS层的薄层电阻相关。结果表明，在氢气气氛中进行热处理会导致电阻率增加（对应于化学计量比的增加），而氧气会引起相反的变化。

著录项

  • 来源
    《Journal of Applied Physics》 |1982年第12期|P.9073-9079|共7页
  • 作者

  • 作者单位
  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种
  • 中图分类
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号