首页> 外文期刊>Journal of Applied Physics >Effect of Hydrostatic Pressure and Temperature on the Magnetic Properties of a Nickel‐Zinc Ferrite
【24h】

Effect of Hydrostatic Pressure and Temperature on the Magnetic Properties of a Nickel‐Zinc Ferrite

机译：静水压力和温度对镍锌铁氧体磁性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Magnetic properties of a nickel-zinc ferrite (15% NiO, 35% ZnO, 50% Fe2O3) were measured over a temperature range of 23°C to 110°C at hydrostatic pressures up to 40 000 psi. The relation between the shift in Curie temperature, ΔTc, and the change in pressure, Δp, was empirically found to be ΔTc=0.078(Δp)0.316. It is shown that if magnetic anisotropy and internal strains limit the magnetizing processes, the relation between coercive force, Hc, maximum flux density, Bm, and initial permeability, μ0, is given by Hc=δBm/μ0, where δ is a proportionality constant. The experimental results obtained over the entire range of temperature and pressure verify the above relation. The value of δ is 2.56 for the ferrite investigated.
机译：镍锌铁氧体（15％NiO，35％ZnO，50％Fe2O3）的磁性能是在23°C至110°C的温度范围内，在高达40 000 psi的静水压力下测量的。根据经验发现居里温度的变化ΔTc与压力变化Δp之间的关系为ΔTc＝ 0.078（Δp）0.316。结果表明，如果磁各向异性和内部应变限制了磁化过程，则矫顽力Hc，最大磁通密度Bm和初始磁导率μ0之间的关系由Hc =δBm/μ0给出，其中δ是比例常数。在整个温度和压力范围内获得的实验结果证明了上述关系。对于研究的铁氧体，δ值为2.56。

著录项

  • 来源
    《Journal of Applied Physics》 |1958年第3期|共2页
  • 作者

    Adams C. Q.; Davis C. M.;

  • 作者单位

    U. S. Naval Ordnance Laboratory, White Oak, Silver Spring, Maryland;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号