We report on a new scintillation crystal, CsCe_2Cl_7, for γ-ray spectroscopy. The crystal was grown using the Czocralski pulling method. X-ray excited luminescence measurements of the CsCe_2Cl_7 showed a broad emission band in the wavelength range from 370 to 470 nm with a peak centre at 410 nm. An energy resolution (FWHM of peak position) for the 662 keV full energy peak of 5.5% was observed at room temperature. The results showed a good proportionality for light output versus y-ray energy. The light output deviation from the linear response is about 10% between the energy range of 31 and 1333 keV. We measured a light yield of 28,000 photons/MeV of absorbed γ-ray energy. The scintillation decay curve of CsCe_2Cl_7 can be described by a single exponential decay function with a decay time of 50 ns. Overall, these measurements clearly indicate that CsCe_2Cl_7 can exhibit attracting scintillation properties, and we believe that the CsCe_2Cl_7 crystal is a promising material for medical imaging and radiation detection.
机译：我们报告了一种新的闪烁晶体CsCe_2Cl_7，用于γ射线光谱学。使用直拉法生长晶体。 CsCe_2Cl_7的X射线激发发光测量显示，在370至470 nm的波长范围内有较宽的发射带，其峰值中心位于410 nm。在室温下，观察到5.5％的662 keV全能量峰的能量分辨率（峰位置的FWHM）。结果表明，光输出与y射线能量成正比。在31和1333 keV的能量范围之间，线性响应的光输出偏差约为10％。我们测得吸收的γ射线能量为28,000光子/ MeV。 CsCe_2Cl_7的闪烁衰减曲线可以用一个衰减时间为50 ns的单指数衰减函数来描述。总体而言，这些测量结果清楚地表明CsCe_2Cl_7可以表现出吸引人的闪烁特性，并且我们认为CsCe_2Cl_7晶体是用于医学成像和放射线检测的有前途的材料。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号