首页> 外文期刊>Journal of Energy Storage >Zinc morphology change in pulsating current deposition
【24h】

Zinc morphology change in pulsating current deposition

机译：脉冲电流沉积中锌的形态变化

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The morphology of Zn deposit can be controlled by pulse deposition. Using defined pulse parameters (20 millisecond-on and 80 millisecond-off), the deposition current density was examined in 50-200 mA cm(-2), in the electrolyte 9 M KOH + 5wt% ZnO, at room temperature (approximately 20 degrees C) on a Zn plate. The obtained Zn morphology is a well-compact boulder microstructure below 100 mA cm(-2). The coulombic efficiency of the deposition is close to 100%. The obtained Zn deposit shows over 90% packing density, with good adhesion to the Zn plate. A change in Zn morphology with deposition time is also observed. The compact boulder microstructure form in the 1 h deposition time becomes a granular spongy Zn after 5 h of deposition.
机译：锌沉积的形态可以通过脉冲沉积来控制。使用定义的脉冲参数（接通20毫秒和断开80毫秒），在室温下（约20℃）在9 M KOH + 5wt％ZnO的电解质中，以50-200 mA cm（-2）检查沉积电流密度℃）。所获得的Zn形态为100 mA cm（-2）以下的紧凑的巨石微结构。沉积的库伦效率接近100％。所获得的锌沉积物显示出超过90％的堆积密度，对Zn板具有良好的附着力。还观察到Zn形态随沉积时间的变化。在1 h的沉积时间内，致密的巨石微结构形式在沉积5 h后变为粒状海绵状Zn。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号