首页> 外文期刊>Journal of Energy Storage >Augmenting the nickel-cobalt layered double hydroxide performance: Virtue of doping
【24h】

Augmenting the nickel-cobalt layered double hydroxide performance: Virtue of doping

机译：增强镍 - 钴层次的双氢氧化物性能：掺杂的美德

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Doping is the most effective strategy to improve the electrochemical performance of supercapacitors. Herein, we report the doping effect of Magnesium on structural instability of Ni-Co LDHs as the supercapacitor electrode material. The morphology of different compositions of magnesium are studied. The derived material with the Ni:Mg ratio of 1:1 displayed an excellent specific capacity of 624 Cg(-1) at current density of 10 Ag-1. Moreover, the specific capacity remained at 80% after 3000 cycles which suggest excellent cycle stability. An asymmetrc device was fabricated with N/M-2 as positive electrode and activated carbon cloth as negative electrode, which displayed a specific capacitance of 200 Fg(-1) at 0.25 Ag-1 with the energy density of 28 Whkg(-1). The device showed the capacitance retention of about 99% after 1000 cycles at 1 Ag-1. Therefore, improved structural
机译：掺杂是提高超级电容器电化学性能的最有效的策略。在此，我们报告了镁对Ni-Co LDHS作为超级电容器电极材料的结构不稳定性的掺杂效果。研究了不同组成的镁的形态。具有Ni：Mg比为1：1的衍生材料在10％Ag-1的电流密度下显示出优异的624cg（-1）的优异特性容量。此外，在3000个循环后，特定容量保持在80％，这表明了良好的循环稳定性。用N / M-2作为正极和活性碳布作为负电极制造的无双滤网，其在0.25Ag-1的比0.25 Whkg（-1）的能量密度显示200fg（-1）的特定电容。 。该器件在1〜Ag-1下循环后，电容保持约为99％。因此，改进了结构

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号