首页> 外文期刊>Journal of Heat Transfer >Fusion Zone Shapes in Electron-Beam Welding Dissimilar Metals
【24h】

Fusion Zone Shapes in Electron-Beam Welding Dissimilar Metals

机译：电子束焊接异种金属的熔合区形状

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Experiments on welding dissimilar metals, such as aluminum or copper to iron with an electron-beam welder, are conducted. It is found that the observed depth-to-width ratio of the fusion zone in aluminum can be greater than unity while that in iron is around unity. The former is attributed to the formation of a cavity result- ing from a high vapor pressure. The difference in depths increases with beam power. The observed depth-to-width ratios of fusion zones in welding copper to iron can be greater than unity.
机译：进行了使用电子束焊机将不同的金属（例如铝或铜）焊接到铁上的实验。发现在铝中观察到的熔合区深宽比可以大于1，而在铁中则可以观察到。前者归因于高蒸汽压导致的空腔形成。深度差随光束功率的增加而增加。在铜和铁的焊接中观察到的熔合区的深宽比可能大于1。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号