首页> 外文期刊>Journal of Materials Engineering and Performance >Influence of Cooling Rate on Transformation Behavior of 0.15% V Microalloyed Steel
【24h】

Influence of Cooling Rate on Transformation Behavior of 0.15% V Microalloyed Steel

机译：冷却速率对0.15％V微合金钢相变行为的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Dilation study was carried out in a thermo-mechanical simulator to understand the phase transformation behavior of a 0.15% vanadium microalloyed steel at three different cooling rates, i.e., 2, 5, and 10 °C/s. Results of the study showed that the phase transformation temperatures, namely Ar3, Ar1, and Bs of 0.15% vanadium microalloyed steel increased with increase in the cooling rate from 2 to 10 °C/s. It was also observed that a cooling rate of 5 °C/s was sufficient to form bainite microstructure in the plates while both bainite and martensite were formed when cooling rate was increased to 10 °C/s. The findings of dilation study were used to design a rolling programme for commercial production of high strength steel plates of 0.15% vanadium steel chemistry.
机译：在热机械模拟器中进行了膨胀研究，以了解0.15％钒微合金钢在三种不同的冷却速率（即2、5和10°C / s）下的相变行为。研究结果表明，0.15％钒微合金钢的相变温度Ar 3 ，Ar 1 和B s 随温度的升高而升高。冷却速度从2提高到10°C / s。还观察到，冷却速率为5°C / s足以在板中形成贝氏体组织，而当冷却速率提高至10°C / s时，贝氏体和马氏体均形成。膨胀研究的结果被用于设计轧制程序，用于商业化生产0.15％钒钢化学成分的高强度钢板。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号