首页> 外文期刊>Journal of Materials Engineering and Performance >Tensile Deformation of a Nickel-base Alloy at Elevated Temperatures
【24h】

Tensile Deformation of a Nickel-base Alloy at Elevated Temperatures

机译：镍基合金在高温下的拉伸变形

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The results of tensile testing involving Waspaloy indicate that the failure strain was gradually reduced at temperatures ranging between ambient and 300 °C. Further, serrations were observed in the engineering stress versus strain diagrams in the temperature range of 300-600 °C. The reduced failure strain and the formation of serrations in these temperature regimes could be the result of dynamic strain aging of this alloy. The extent of work hardening due to plastic deformation was reduced at temperatures above 300 °C. A combination of ductile and intergranular brittle failures was seen at temperatures above 600 °C. γ′ was detected at all tested temperatures.
机译：涉及Waspaloy的拉伸试验结果表明，在环境温度和300°C之间的温度下，破坏应变逐渐降低。此外，在300-600°C的温度范围内，在工程应力与应变图中观察到锯齿。在这些温度范围内降低的失效应变和形成锯齿可能是该合金动态应变时效的结果。在高于300°C的温度下，由于塑性变形而导致的加工硬化程度降低了。在高于600°C的温度下观察到韧性和晶间脆性破坏的组合。在所有测试温度下均检测到γ'。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号