首页> 外文期刊>Journal of Materials Engineering and Performance >Designing sealing glasses for solid oxide fuel cells
【24h】

Designing sealing glasses for solid oxide fuel cells

机译：设计用于固体氧化物燃料电池的密封玻璃

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Thermal and chemical properties of “invert” glasses and glass-ceramics developed for hermetic seals for solid oxide fuel cells are described. The glasses crystallize to form thermally stable pyro- and orthosilicate phases with the requisite thermal expansion match to the Y-stabilized ZrO2 (YSZ) electrolyte. In addition, the glasses bond to Cr-steel substrates at 800–850 °C without forming extensive interfacial reaction products. The thermal expansion characteristics of the glass-ceramics remain essentially unchanged after 28 days at 750 °C. Compositions with lower (≤2 mol%) B2O3 contents exhibit the lowest volatilization rates when exposed to wet forming gas at 750 °C.
机译：描述了为固体氧化物燃料电池的气密密封而开发的“倒置”玻璃和玻璃陶瓷的热和化学性质。玻璃结晶后形成热稳定的焦硅酸盐和原硅酸盐相，其热膨胀与Y稳定的ZrO2 （YSZ）电解质相匹配。此外，玻璃在800–850°C的温度下结合到Cr钢基底上，而不会形成大量的界面反应产物。在750°C下28天后，玻璃陶瓷的热膨胀特性基本保持不变。 B2 O3 含量较低（≤2mol％）的组合物在750°C下暴露于湿的成型气体中时，挥发速率最低。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号