首页> 外文期刊>Journal of Materials Engineering and Performance >Control of Recrystallization during High-Temperature Hot-Rolling of Grain-Oriented Silicon Steel
【24h】

Control of Recrystallization during High-Temperature Hot-Rolling of Grain-Oriented Silicon Steel

机译：取向硅钢高温热轧过程中的再结晶控制

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Recrystallization kinetics of 3% Si steel after hot rolling in the temperatures between 1373 and 1573 K, which is quite important to obtain uniform magnetic properties, was studied. Recrystallization rate after hot rolling was relatively slow because of low dislocation density, which resulted from rapid recovery, and its behavior was strongly influenced by the initial grain size and coexistence of the yphase. Based on these findings, controlling technology of recrystallization during hot rolling of grain-oriented Si steels is discussed.
机译：研究了3％Si钢在1373 K和1573 K之间的温度下热轧后的再结晶动力学，这对于获得均匀的磁性能非常重要。热轧后的重结晶速率较低，这是由于位错密度低，这是由于快速恢复所致，并且其行为受到初始晶粒尺寸和y相共存的强烈影响。基于这些发现，讨论了取向硅钢热轧过程中再结晶的控制技术。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号