首页> 外文期刊>Journal of Materials Research >A new route to single crystalline vanadium dioxide nanoflakes via thermal reduction
【24h】

A new route to single crystalline vanadium dioxide nanoflakes via thermal reduction

机译：通过热还原制取单晶二氧化钒纳米薄片的新途径

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Large-area single-crystalline vanadium dioxide nanoflakes were first fabricated via a thermal reduction method in a tube furnace. The sample was characterized by x-ray diffraction, x-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The results show that VO_2 nanoflakes are single-crystalline with a monoclinic structure. The VO_2 nanoflakes have a width of 200-300 nm, a thickness of 50-100 nm, and a length up to 1-2 μm. It is found that single-crystalline VO_2 nanoflakes show a novel and complicated 5-7-step Li-storage behavior for an insertion amount of <0.6 mol lithium per mol of VO_2.
机译：首先在管式炉中通过热还原法制备大面积的单晶二氧化钒纳米薄片。通过X射线衍射，X射线光电子能谱，扫描电子显微镜和透射电子显微镜对样品进行表征。结果表明，VO_2纳米片为单晶，具有单斜晶结构。 VO_2纳米薄片的宽度为200-300 nm，厚度为50-100 nm，长度最大为1-2μm。发现单晶VO_2纳米薄片显示出新颖且复杂的5-7步锂存储行为，其中每摩尔VO_2的插入量小于0.6摩尔锂。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号