首页> 外文期刊>Journal of Materials Research >A new high-strength spinodal alloy
【24h】

A new high-strength spinodal alloy

机译：新型高强度旋节线合金

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Preliminary investigations of a new high-strength alloy of composition Fe_(30)Ni_(20)Mn_(25)Al_(25) (at.percent) are described in this paper. The as-cast alloy consisted of a periodic two-phase microstructure of interconnected, ~50-nm-wide rods with fully coherent {100} interfaces, strongly suggestive of formation by a B2 to [(B2 + body-centered cubic (bcc)) spinodal decomposition. The (Ni, Al)-rich B2 and (Fe, Mn)-rich bcc phases differed in lattice parameter by <0.5 percent. Hardness and yield strength of the as-cast alloy were found to be approximately 500 VPN and 1500 MPa, respectively, and increased by more than 50 percent after annealing at 550 deg C for several days. (Fe, Mn)-rich precipitates with a (3-Mn structure were observed in the annealed material.
机译：本文介绍了一种新的组成为Fe_（30）Ni_（20）Mn_（25）Al_（25）（at。％）的高强度合金的研究。铸态合金由相互连接的〜50nm宽的棒具有周期性的两相微观结构组成，棒具有完全相干的{100}界面，强烈暗示了B2形成为[（B2 +体心立方（bcc） ）旋节线分解。富（Ni，Al）的B2相和富（Fe，Mn）的bcc相的晶格参数相差<0.5％。发现铸态合金的硬度和屈服强度分别约为500 VPN和1500 MPa，在550℃退火几天后，其硬度增加了50％以上。在退火材料中观察到具有（3-Mn结构）的富（Fe，Mn）沉淀。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号