首页> 外文期刊>Journal of Materials Research >Solution-based processing of Sc_2O_3 nanopowders yielding transparent ceramics
【24h】

Solution-based processing of Sc_2O_3 nanopowders yielding transparent ceramics

机译：基于溶液的Sc_2O_3纳米粉的加工产生透明陶瓷

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A basic sulfate precursor [Sc(OH)SO_4 centre dot 2H_2O] for well-sinterable Sc_2O_3 powders was precipitated from mixed solutions of scandium nitrate [Sc(NO_3)_3] and ammonium sulfate [(NH_4)_2SO_4] at room temperature and which was subsequently converted to Sc_2O_3 via dehydroxylization and desulfurization at temperatures >=900 deg C. With the reactive powders synthesized in this work, polycrystalline Sc_2O_3 ceramics showing high inline transmittances of approximately 70 percent in the visible wavelength region (corresponding to approx 90 percent of the theoretical value of single crystals) have been fabricated via vacuum sintering at a relatively low temperature of 1700 deg C.
机译：在室温下，从硝酸scan [Sc（NO_3）_3]和硫酸铵[（NH_4）_2SO_4]的混合溶液中沉淀出易于烧结的Sc_2O_3粉末的碱性硫酸盐前体[Sc（OH）SO_4中心点2H_2O]。随后在> = 900℃的温度下通过脱羟基和脱硫将其转化为Sc_2O_3。利用这项工作中合成的反应性粉末，多晶Sc_2O_3陶瓷在可见波长范围内显示出大约70％的高在线透射率（相当于理论值的大约90％）。通过真空烧结在1700摄氏度的相对较低的温度下制得了单晶硅（单晶）。

著录项

  • 来源
    《Journal of Materials Research》 |2004年第3期|p.733-736|共4页
  • 作者

    Ji-Guang Li; Takayasu Ikegami; Toshiyuki Mori;

  • 作者单位

    Advanced Materials Laboratory, National Institute for Materials Science, Namiki 1-1, Tsukuba, Ibaraki 305-0044, Japan;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 工程材料学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号