首页> 外文期刊>Journal of Materials Research >Bulk glass formation in an Fe-based Fe-Y-Zr-M (M = Cr, Co, Al)-Mo-B system
【24h】

Bulk glass formation in an Fe-based Fe-Y-Zr-M (M = Cr, Co, Al)-Mo-B system

机译：铁基Fe-Y-Zr-M（M = Cr，Co，Al）-Mo-B系统中的块状玻璃形成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Several new bulk metallic glasses based on Fe-Y-Zr-(Co, Cr, Al)-Mo-B, which have a glass-forming ability superior to the best composition Fe_(61)Zr_(10)Co_7Mo_5W_2B_(15) reported recently, have been successfully developed. The as-cast bulk amorphous alloys showed a distinctly high thermal stability with glass-transition temperatures above 900 K, supercooled liquid regions above 60 K, and high strength with Vickers hardness values larger than HV 1200. The suppression of the growth of primary phases in the molten liquids and the resultant low liquidus temperatures were found to be responsible for the superior glass-forming ability in these new alloys. It was found that the addition of 2 percent Y not only facilitated bulk glass formation, but the neutralizing effect of Y with oxygen in the molten liquids also improved the manufacturability of these amorphous alloys.
机译：报道了几种基于Fe-Y-Zr-（Co，Cr，Al）-Mo-B的新型块状金属玻璃，其玻璃形成能力优于最佳成分Fe_（61）Zr_（10）Co_7Mo_5W_2B_（15）最近，已经成功开发。铸态块状非晶态合金具有明显的高热稳定性，玻璃化转变温度高于900 K，过冷液体区域高于60 K，并且具有高强度，维氏硬度值大于HV 1200。人们发现，熔融液体和较低的液相线温度是这些新型合金优异的玻璃形成能力的原因。发现添加2％的Y不仅促进了块状玻璃的形成，而且Y与熔融液体中的氧的中和作用也改善了这些非晶态合金的可制造性。

著录项

  • 来源
    《Journal of Materials Research》 |2004年第3期|p.921-929|共9页
  • 作者

    Z.P. Lu; C.T. Liu; C.A. Carmichael;

  • 作者单位

    Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6115;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 工程材料学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号