首页> 外文期刊>Journal of Materials Research >Micro-indentation of aluminum processed by equal channel angular extrusion
【24h】

Micro-indentation of aluminum processed by equal channel angular extrusion

机译：等通道角挤压加工的铝微压痕

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The near-surface deformation of equal-channel angular extruded (ECAE) pure aluminum was investigated using the micro-indentation technique. Compared with fully annealed Al samples, there is a distinguishable difference in the indentation deformation. The unloading slope of the ECAE deformed Al after a short unloading period was found to be less than that of the annealed samples due to plastic recovery. Work hardening was observed, which depended on the history of local deformation. A new relationship between the plastic energy dissipated in the indentation and the applied load was derived, which is supported by the experimental results.
机译：使用微压痕技术研究了等通道角挤压（ECAE）纯铝的近表面变形。与完全退火的铝样品相比，压痕变形存在明显区别。由于塑性恢复，发现短时间卸载后ECAE变形Al的卸载斜率小于退火样品的卸载斜率。观察到加工硬化，这取决于局部变形的历史。得出了压痕中耗散的塑性能量与施加的载荷之间的新关系，这得到了实验结果的支持。

著录项

  • 来源
    《Journal of Materials Research》 |2004年第4期|p.1243-1248|共6页
  • 作者

    Fuqian Yang; Lingling Peng; Kenji Okazaki;

  • 作者单位

    Department of Chemical and Materials Engineering, University of Kentucky, Lexington, Kentucky 40506;

  • 收录信息 美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 工程材料学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号