首页> 外文期刊>Journal of materials science >Pb/S/1,2-ethanedithiol composite thin films for efficient solid-state quantum-dot sensitized TiO_2 nanorod array solar cells
【24h】

Pb/S/1,2-ethanedithiol composite thin films for efficient solid-state quantum-dot sensitized TiO_2 nanorod array solar cells

机译：用于高效固态量子点敏化的TiO_2纳米棒阵列太阳能电池的Pb / S / 1,2-乙二硫醇复合薄膜

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The Pb/S/1,2-ethanedithiol composite thin films were successfully deposited on TiO~(2)nanorod arrays by spin-coating step-by-step 5 mmol dm_(−3)Pb(NO~(3))~(2), Na~(2)S and 1% 1,2-ethanedithiol solution and their chemical compositions can be easily adjusted by changing the concentration of Na~(2)S solution from 5 to 3.5 mmol dm_(−3)and 2 mmol dm_(−3). The average crystal sizes of Pb/S/1,2-ethanedithiol quantum-dots decreased from 7.9 to 7.1 nm and 6.5 nm with the decrease of the concentration of Na~(2)S solution and the chemical bonding of Pb_(2+)and S in EDT was chelation of the penta-heterocycle in Pb/S/1,2-ethanedithiol composite thin films. All solid-state Pb/S/1,2-ethanedithiol composite thin film sensitized TiO~(2)nanorod array solar cells using 5, 3.5, 2 mmol dm_(−3)Na~(2)S solution exhibited the photoelectric conversion efficiency of 2.68, 3.41 and 4.51% under the illumination of simulated AM 1.5 sunlight (100 mA cm_(−2)).
机译：通过分步旋涂5mmol dm _（-3）Pb（NO〜（3））〜（）成功地将Pb / S / 1,2-乙二硫醇复合薄膜沉积在TiO〜（2）纳米阵列上。 2），Na〜（2）S和1％1,2-乙二硫醇溶液及其化学组成可以通过将Na〜（2）S溶液的浓度从5更改为3.5 mmol·dm _（− 3）和2来轻松调节摩尔dm _（-3）。随着Na〜（2）S溶液浓度的降低和Pb_（2+）的化学键的降低，Pb / S / 1,2-乙二硫醇量子点的平均晶体尺寸从7.9nm降至7.1nm和6.5nm EDT中的S是Pb / S / 1,2-乙二硫醇复合薄膜中五杂环的螯合。使用5、3.5、2 mmol·dm _（-3）Na〜（2）S溶液的所有固态Pb / S / 1,2-乙二硫醇复合薄膜敏化TiO〜（2）纳米阵列太阳能电池均表现出光电转换效率在模拟的AM 1.5阳光（100mA cm _（− 2））的光照下分别为2.68、3.41和4.51％