Synthesis and Antimicrobial Activity of Fe:TiO_2 Particles

机译：Fe：TiO_2的合成及抑菌活性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

TiO2 and iron-doped TiO2 were synthesized by sol-gel method. TiO(2 )and 0.5 %mol Fe:TiO2 were calcined at 500 and 800 degrees C for 3 h. The synthesized particles were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), UV-VIS diffuse reflectance spectrophotometry (UV/DRS), scanning electron microscopy (SEM) and scanning electron microscope-energy dispersive X-Ray analysis (SEM-EDX). The XRD patterns of all samples that were calcined at 500 degrees C showed only anatase phase. On increasing temperature from 500 to 800 degrees C, the anatase phase transformed to rutile phase. For 0.5 %mol Fe:TiO2, pseudobrookite (Fe2TiO5) phase was observed at 800 degrees C. The particles that contained rutile showed higher antibacterial activities against E. coli, B. subtilis, and S. aureus than anatase phase, under fluorescent irradiation.
机译：采用溶胶-凝胶法合成了TiO2和铁掺杂的TiO2。 TiO（2）和0.5％mol Fe：TiO2在500和800摄氏度下煅烧3小时。通过X射线衍射（XRD），傅立叶变换红外光谱（FT-IR），UV-VIS漫反射分光光度法（UV / DRS），扫描电子显微镜（SEM）和扫描电子显微镜-能量色散X来表征合成的颗粒。 -射线分析（SEM-EDX）。在500摄氏度下煅烧的所有样品的XRD图谱仅显示锐钛矿相。在将温度从500摄氏度提高到800摄氏度时，锐钛矿相转变为金红石相。对于0.5％mol的Fe：TiO2，在800摄氏度时观察到假板钛矿（Fe2TiO5）相。在荧光照射下，含有金红石的颗粒比锐钛矿相具有更高的对大肠杆菌，枯草芽孢杆菌和金黄色葡萄球菌的抗菌活性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号