首页> 外文期刊>Journal of Polymers and the Environment >A Facile Chemical Approach to Isolate Cellulose Nanofibers from Jute Fibers
【24h】

A Facile Chemical Approach to Isolate Cellulose Nanofibers from Jute Fibers

机译：一种容易化学方法，用于从黄麻纤维中脱离纤维素纳米纤维

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this work, Jute fibers (JF) were directly treated with HNO3-NaNO2 (JF/HNO3-NaNO2) mixture and simultaneously with NaOH and HNO3-NaNO2 (JF/NaOH/HNO3-NaNO2) mixture successively to extract cellulose nanofibers (CNFs) in a facile and cost-effective manner. Chemical composition, Morphological, structural, spectroscopic, and thermal analysis was carried out. TEM analysis of CNFs synthesized via JF/NaOH/HNO3-NaNO2 and JF/HNO3-NaNO2 showed an average diameter of 7-9 nm and 9-11 nm, respectively. CNFs obtained from alkali treated fibers possessed remarkable crystallinity of 63.9% as compared to 55.5% from raw fibers. Coexistence of both cellulose I and cellulose II type structures in CNFs via. JF/NaOH/HNO3-NaNO2 marks its inexhaustive applicability in industrial sectors.
机译：在这项工作中，用HNO3-纳米2（JF / HNO3-NANO2）混合物直接用HNO3-纳米（JF / HNO3-NANO2）混合物直接用NaOH和HNO3-纳米2（JF / NaOH / HNO 3-NaNO 2）混合物，以提取纤维素纳米纤维（CNFS）的同时处理以容易和成本效益的方式。进行化学成分，形态学，结构，光谱和热分析。通过JF / NaOH / HNO3-NANO2和JF / HNO3-NANO 2合成的CNF的TEM分析分别显示平均直径为7-9nm和9-11nm。从碱处理纤维中获得的CNF具有显着的结晶度为63.9％，与原料纤维的55.5％相比。纤维素I和纤维素II型结构在CNFS中共存。 JF / NaOH / HNO3-Nano2标志着其在工业领域的无穷无尽的适用性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号