首页> 外文期刊>Journal of power sources >Poly (vinylidene fluoride-co-hexafluoropropylene)/polybenzimidazole blend nanofiber supported Nafion membranes for direct methanol fuel cells
【24h】

Poly (vinylidene fluoride-co-hexafluoropropylene)/polybenzimidazole blend nanofiber supported Nafion membranes for direct methanol fuel cells

机译：直接甲醇燃料电池用聚偏氟乙烯/六氟丙烯共聚物/聚苯并咪唑共混纳米纤维支撑的Nafion膜

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This article presents preparation of poly (vinylidene fluoride-co-hexarluoropropylene) (PvdF-co-HFP) and polybenzimidazole (PBI) blend electrospun nanofiber (PVFP-BI) films from N,N'-dimethyl acetamide (DMAc)/acetone mixture solutions. Using the PVFP-BI nanofiber film (thickness ～ 13-15 μm) as a supporting material for impregnating Nafion resin solution, Nafion/PVFP-BI composite membranes (thickness ～50 μm) are prepared and direct methanol fuel cell (DMFC) tests are performed. Better DMFC performance of the Nafion/PVFP-BI composite membrane than the commercial Nafion-117 (thickness ～ 175 μm) and Nafion-212 (thickness ～ 50 μm) membranes when blending with 5-10 wt.% of PBI in the PVFP-BI nanofiber support film is demonstrated.
机译：本文介绍了由N，N'-二甲基乙酰胺（DMAc）/丙酮混合溶液制备聚（偏二氟乙烯-共六氟丙烯）（PvdF-co-HFP）和聚苯并咪唑（PBI）共混电纺纳米纤维（PVFP-BI）薄膜的方法。 。以PVFP-BI纳米纤维膜（厚度〜13-15μm）作为浸渍Nafion树脂溶液的支撑材料，制备了Nafion / PVFP-BI复合膜（厚度〜50μm），并进行了直接甲醇燃料电池（DMFC）测试。执行。当与5-10 wt。％的PBI在PVFP-PP中共混时，Nafion / PVFP-BI复合膜的DMFC性能优于市售的Nafion-117（厚度〜175μm）和Nafion-212（厚度〜50μm）膜。展示了BI纳米纤维支撑膜。