摘要

Yttrium-doped barium cerate, BaCe_(0.85) Y_(0.15)O_(3-α) (BCY15), membranes are proton-conducting electrolytes for intermediate-temperature protonic ceramic fuel cells (IT-PCFC), useful for, among other processes, co-production of power and ethylene by dehydrogenation of ethane. BCY15 membranes showed good conductivity at intermediate temperatures, 15 and 20 mS cm~(-1) at 700 and 750 ℃, respectively. Maximum power density was 174 mW cm~(-2) at 700 ℃, with a corresponding current density of 320 mA cm~(-2), using a C_2H_6,Pt/BCY15/Pt,O_2 fuel cell, with a ca. 0.5 mm thick membrane, producing 34% ethane conversion with 96% ethylene selectivity Comparison of performances using vertical and horizontal set-ups showed that horizontal set-ups are subject to torsional strain, causing reduced cell performance resulting from even minor leakage at the glass seal.
机译：掺钇的铈酸钡BaCe_（0.85）Y_（0.15）O_（3-α）（BCY15）是用于中温质子陶瓷燃料电池（IT-PCFC）的质子传导电解质，可用于其他工艺，通过乙烷脱氢联产电力和乙烯。 BCY15膜在700和750℃的中温下分别具有15和20 mS cm〜（-1）的电导率。使用C_2H_6，Pt / BCY15 / Pt，O_2燃料电池，在700℃时，最大功率密度为174 mW cm〜（-2），相应的电流密度为320 mA cm〜（-2）。 0.5毫米厚的膜，可产生34％的乙烷转化率和96％的乙烯选择性使用垂直和水平装置进行的性能比较显示，水平装置会受到扭转应变，导致玻璃密封件即使有很小的渗漏也会导致电池性能下降。 。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号