首页> 外文期刊>The Journal of the Textile Institute >Soft body armour development by silica particle based shear thickening fluid coated p-aramid fabrics
【24h】

Soft body armour development by silica particle based shear thickening fluid coated p-aramid fabrics

机译：基于二氧化硅颗粒的剪切增稠流体涂层P-芳纶织物的软体铠装

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Soft body armour panels using p-aramid (Technora) fabrics with three different levels of thread densities were developed in this research. Shear thickening fluid (STF) was synthesized using silica nano-particle (100 nm) and polyethylene glycol (PEG). Fabrics were coated with 60% (w/w) STF to improve their resistance against low-velocity bullets (165 m s(-1)). For neat fabrics, all the bullets fired from 0.38 '' calibre revolver pierced the multilayer fabric panel. However, impact energy absorption increased with the increase in thread density in fabric. After coating with shear thickening fluid, panels having four layers of fabric stopped all the bullets fired. It was possible to reduce the weight of panel by 23% after the STF treatment whilst ensuring bullet stoppage.
机译：在这项研究中开发了使用具有三种不同螺纹密度的P-Aramid（Technora）织物的软体护甲面板。使用二氧化硅纳米颗粒（100nM）和聚乙二醇（PEG）合成剪切增稠液（STF）。涂有60％（w / w）STF的织物，以改善它们对低速子弹的阻力（165 m s（-1））。对于洁面的织物，所有子弹从0.38''口径旋转手枪射击，刺穿了多层织物面板。然而，随着织物中的螺纹密度的增加，冲击能量吸收增加。在用剪切增稠液涂覆后，具有四层织物的面板停止了所有引发的子弹。在STF治疗后，可以将面板的重量减少23％，同时确保子弹停止。