首页> 外文期刊>The Journal of the Textile Institute >A foam single-face pretreatment to modify silk fabric using EBODAC to improve inkjet printing performance
【24h】

A foam single-face pretreatment to modify silk fabric using EBODAC to improve inkjet printing performance

机译：使用EBODAC进行泡沫单面预处理以修饰真丝织物，以改善喷墨打印性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A novel foam single-face pretreatment was used to modify silk fabrics for improving inkjet printing performance without any washing process. The foams used in pretreatment process were prepared by foaming agent, as Tween 80 and Sodium dodecyl sulfate (SDS). The compatibilities of the cationic modifier ethylene base-double octadecyl dimethyl ammonium chloride (EBODAC) agent with Tween 80 and SDS were investigated by comparing the foam properties at different EBODAC concentrations. The results show that Tween 80 is more compatible with EBODAC. The silk fabric surface is adhered with cationic groups after foam-treated with EBODAC, which improves the inkjet printing performances. The K/S values enhance from 5.84 to 8.21 with the increasing EBODAC concentrations. The printing images of treated fabrics perform more vivid than those of the controlled silk fabrics. The width and edges of practical printing lines become smaller and more definite, respectively. All these indicate that higher color yield and definition are achieved. The hand feeling after foam pretreatment is superior to that after pad pretreatment. The fastnesses are hardly affected after pretreatment. The foam-pretreatment provides a new pathway to improve the inkjet printing performance.
机译：一种新颖的泡沫单面预处理用于修饰真丝织物，以提高喷墨打印性能，而无需任何洗涤过程。预处理过程中使用的泡沫是由吐温80和十二烷基硫酸钠（SDS）制成的。通过比较不同EBODAC浓度下的泡沫性能，研究了阳离子改性剂乙烯基双十八烷基双甲基氯化铵（EBODAC）与Tween 80和SDS的相容性。结果表明Tween 80与EBODAC更加兼容。用EBODAC进行泡沫处理后，丝绸织物表面粘附有阳离子基团，从而改善了喷墨打印性能。随着EBODAC浓度的增加，K / S值从5.84提高到8.21。经过处理的织物的印刷图像比受控的真丝织物的印刷图像更生动。实际印刷线的宽度和边缘分别变得更小和更确定。所有这些表明，实现了更高的颜色产量和清晰度。泡沫预处理后的手感优于垫预处理后的手感。预处理后牢度几乎不受影响。泡沫预处理为改善喷墨打印性能提供了新途径。

著录项

  • 来源
    《The Journal of the Textile Institute》 |2014年第8期|799-805|共7页
  • 作者

    Qiankun Shen; Shaoyu Chen; Chaoxia Wang; Chunyue Liu; Anli Tian;

  • 作者单位

    Key Laboratory of Eco-Textile, Ministry of Education, Jiangnan University, Wuxi, P.R. China;

    Key Laboratory of Eco-Textile, Ministry of Education, Jiangnan University, Wuxi, P.R. China;

    Key Laboratory of Eco-Textile, Ministry of Education, Jiangnan University, Wuxi, P.R. China;

    Key Laboratory of Eco-Textile, Ministry of Education, Jiangnan University, Wuxi, P.R. China;

    Key Laboratory of Eco-Textile, Ministry of Education, Jiangnan University, Wuxi, P.R. China;

  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类
  • 关键词

    foam pretreatment; single-face; inkjet printing; cationic; silk;

    机译：泡沫预处理;单面喷墨印刷;阳离子丝;