By the unique crazing process with sharp bending and tensile stress, the voids of the crazes were generated in polypropylene (PP) and polystyrene (PS) films. The tensile strength of the crazed PP and PS films was almost unchanged after the crazing processing, while Young's modulus decreased with the crazing tension increasing. The gas permeability of all the PP and PS films increased with the crazing tension because of the increase in void fraction. The crazes of PP and PS films penetrated completely in the direction of film thickness above 4 N/cm and 5 N/cm, respectively, of the crazing tension. Permeation model was proposed on the basis of the relationship between the measured gas permeability and the void fraction in the films. The gas permeability of the crazed films was estimated by the combination of the parallel and the series models which were constituted of the crazed and non-crazed regions in parallel or serial order in the direction of gas permeation.%プラスチック製品に無理な力を加えたり，フイルムに折り目を付けたりすると，その部分が白化することがよくある．これは，クレージング現象であり，その商品が初期破壊状態にあることを示す．高分子材料のクレーズは，内部がナノ～サブミクロンオーダの小繊維（フィブリル）とポイドからなるスポンジに似た構造を有する．ポイドは光を良く散乱するため，クレージングした高分子フイルムは白色に見える．
机译：通过具有急剧弯曲和拉伸应力的独特开裂工艺，在聚丙烯（PP）和聚苯乙烯（PS）薄膜中产生了裂纹。裂纹处理后的PP和PS薄膜的拉伸强度几乎没有变化，而杨氏模量随裂纹张力的增加而降低。由于空隙率的增加，所有PP和PS膜的透气性都随着开裂张力的增加而增加。 PP和PS膜的裂纹分别在裂纹强度高于4 N / cm和5 N / cm的膜厚度方向上完全渗透。根据所测得的气体渗透率与薄膜中空隙率之间的关系，提出了一种渗透模型。裂纹膜的透气度是通过平行和串联模型的组合来估计的，该平行和串联模型是由平行和连续的，沿气体渗透方向按顺次或顺次区域构成的裂纹区域和非裂纹区域组成的。加これは，フイルムに折り目を付けたりすると，その部分が白化することがよくある。これは，クレージング现象であり，その商品が初期破壊状态にあることを示す。高分子材料のクレーズは，内部が繊〜サブミクロンオーダの小繊维（フィブリル）とポイドからなるスポンポ似た构造を有する。ポイドは光を良く散乱するため，クレージングした高分子フイルムは白色に见える。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号