首页> 外文期刊>繊維学会誌 >エレクトロスピニング法により作製したポリジオキサノンナノファイバーの構造研究
【24h】

エレクトロスピニング法により作製したポリジオキサノンナノファイバーの構造研究

机译：静电纺丝法制备聚二恶烷酮纳米纤维的结构研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nanofibers of polydioxanone (PPDX) were electrospun from 3.0-wt% solution in 1,1,1,3,3,3-hexafluoro-2-propanol. Structure and morphology of the electrospun nanofibers were investigated by transmission electron microscopy (TEM). In order to align and collect nanofibers parallel to each other, we used a homemade collector with separated electrodes which was specially designed. TEM revealed that thus aligned nanofibers on the collector are partially crystallized. The SAED patterns of nanofibers, which were drawn and/or heat-treated with being deposited on the collector, showed a well-developed fiber pattern. In the dark-field image of heat-treated nanofibers, many striations which are running perpendicular to the fiber axis were observed. These striations appear to be a part of stacked-lamellar structure oriented in the direction of fiber axis. This result indicated that heat-treated PPDX nanofibers have stacked-lamellar structure.%生体吸収性高分子を用いた医療材料の開発が盛んに行 われており，再生医療分野への利用に向け，生体吸収性 高分子の物性・分解性の制御はますます重要になると考 えられる．生休吸収性高分子として，ポリグリコール 酸（PGA），ポリ乳酸（PLA），ならびにそれらの共重合体 が挙げられるが，材料として優れた柔軟性と適度な分解 速度を有するという利点から，ポリジオキサノン（PPDX） が注目されている．
机译：将聚二恶烷酮（PPDX）的纳米纤维从3.0重量％的1,1,1,3,3,3-六氟-2-丙醇溶液中进行电纺丝。通过透射电子显微镜（TEM）研究了电纺纳米纤维的结构和形态。为了对齐和收集彼此平行的纳米纤维，我们使用了经过特殊设计的带有分离电极的自制收集器。 TEM显示，由此在收集器上排列的纳米纤维被部分结晶。通过沉积在收集器上进行拉伸和/或热处理的纳米纤维的SAED图案显示出完善的纤维图案。在热处理的纳米纤维的暗场图像中，观察到许多垂直于纤维轴的条纹。这些条纹似乎是沿纤维轴方向定向的叠层结构的一部分。该结果表明，经热处理的PPDX纳米纤维具有层叠的层状结构。の物性・分解性の制御はますます重要になると考えられる。生休吸收性高分子として，ポリグリコール酸（PGA），ポリ乳酸（PLA），ならびにそれらの共重合体が挙げられるが，材料として优れた柔软性と适度な分解速度を有するという利点から，ポリジオキサノン（PPDX）が注目されている。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号