首页> 外文期刊>Journal of University of Science and Technology Beijing >Thermodynamic behavior of manganese and phosphorus between liquid iron and CaO-MgO-SiO_2-Al_2O_3-Fe_To-MnO-P_2O_5 slags
【24h】

Thermodynamic behavior of manganese and phosphorus between liquid iron and CaO-MgO-SiO_2-Al_2O_3-Fe_To-MnO-P_2O_5 slags

机译：液态铁与CaO-MgO-SiO_2-Al_2O_3-Fe_To-MnO-P_2O_5炉渣之间锰和磷的热力学行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The thermodynamic behavior of manganese and phosphorus between liquid iron and CaO-MgO-SiO_2-Al_2O_3-Fe_tO_MnO-P_2O_5 ladle slag system was addresed by investigating the thermodynamic equilibria between liquid iron containing Mn and P and the ladle slag at 1 873 K. The Mn distribution ratio L_Mn increases with increasing Fe_tO content and decreasing the basicity(/100 CaO + /100 MgO)/ (/100 SiO + /100 Al_2O_3 + /100 P_2O_5)in slag, while the P distribution ratio L_p seems to be increased as Fe_tO content and the basicity increases.
机译：通过研究含Mn和P的液态铁与钢包渣在1 873 K时的热力学平衡，增加了铁水和CaO-MgO-SiO_2-Al_2O_3-Fe_tO_MnO-P_2O_5钢包渣系统中锰和磷的热力学行为。分布比L_Mn随着Fe_tO含量的增加和碱度的降低而降低（/ 100 CaO + / 100 MgO）/（/ 100 SiO + / 100 Al_2O_3 + / 100 P_2O_5），而P分布比L_p似乎随着Fe_tO的增加而增加内容和碱性增加。