首页> 外文期刊>Kawasaki Steel Technical Report >TS 540—780 N/mm~2 Grade Hot-Rolled Steel Sheets with Good Formability and High Fatigue Strength, 'RHA 540 DH—RHA 780 DH'
【24h】

TS 540—780 N/mm~2 Grade Hot-Rolled Steel Sheets with Good Formability and High Fatigue Strength, 'RHA 540 DH—RHA 780 DH'

机译：TS 540—780 N / mm〜2级具有良好成形性和高疲劳强度的热轧钢板，'RHA 540 DH-RHA 780 DH'

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A large quantity of hot-rolled high-strength steel sheets have been used in automotive chassis parts to reduce weight. When thinner sheets are adopted for further weight reduction, their press formability and fatigue strength must be improved. This paper reports on the features of the TS 540-780 N/mm~2 grade hot-rolled high-strength steel sheet developed by Kawasaki Steel for improvement of the above characteristics, based on a new microstructural control method.
机译：大量的热轧高强度钢板已用于汽车底盘部件以减轻重量。当采用较薄的片材以进一步减轻重量时，必须提高其压制成形性和疲劳强度。本文基于一种新的微观组织控制方法，对川崎钢铁公司为改善上述性能而开发的TS 540-780 N / mm〜2级热轧高强度钢板的特点进行了报道。