首页> 外文期刊>Key Engineering Materials >Effect of CNTs on Property of Calcium Phosphate Cement
【24h】

Effect of CNTs on Property of Calcium Phosphate Cement

机译：碳纳米管对磷酸钙水泥性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effect of carbon nanotubes (CNTs) on bending strength of calcium phosphate cement was investigated. The cement composite powders, containing 0, 0.2%, 0.4%, 0.6%, 0.8% and 1.0wt% CNTs respectively, were prepared by ball milling. It was found that the presence of CNTs improved the bending strength of the cement from 6.6 MPa to the best 10.5 MPa. The reason for mechanical property improvement is related to the fibers (bars)-like microstructure of the reinforcing element, with CNT in the core and hydroxyapatite crystals growing on it.
机译：研究了碳纳米管（CNTs）对磷酸钙水泥弯曲强度的影响。通过球磨制备分别包含0、0.2％，0.4％，0.6％，0.8％和1.0wt％的CNT的水泥复合粉末。发现碳纳米管的存在将水泥的弯曲强度从6.6 MPa提高到最佳的10.5 MPa。改善机械性能的原因与增强元件的纤维（棒）状微观结构有关，核心中具有CNT，并且在其上生长有羟基磷灰石晶体。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号