首页> 外文期刊>Key Engineering Materials >Damping Characteristics of Cold-Rolled and Annealed Equiatomic TiNi Shape Memory Alloy
【24h】

Damping Characteristics of Cold-Rolled and Annealed Equiatomic TiNi Shape Memory Alloy

机译：冷轧退火等原子TiNi形状记忆合金的阻尼特性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Damping capacity and storage modulus of cold-rolled and annealed TisoNiso SMA are systematically investigated by DSC and DMA tests. The specimens annealed at 500℃ for 1 ～ 72 h and annealed at 650℃ for short time can all reach a high tan δ value and a deep storage modulus minimum during B2→R transformation. This reveals that the occurrence of R-phase can strongly soften the storage modulus and thus promote the damping capacity of Ti_(50)Ni_(50) SMA. The specimens anneaed at 650℃ fpr longer time have a lower tan δ value due to the diminishing of R-phase formation. Therefore, a good damping capacity associated with a significant softening storage modulus can be acquired by suitably control the annealing conditions of cold-rolled Ti_(50)Ni_(50) to generate adequate of R-phase premartensite.
机译：通过DSC和DMA测试系统地研究了冷轧和退火的TisoNiso SMA的阻尼能力和储能模量。在B2→R转变过程中，在500℃下退火1〜72 h，在650℃下短时间退火的试样都可以达到较高的tanδ值和极小的储能模量。这表明，R相的出现可以大大软化储能模量，从而提高Ti_（50）Ni_（50）SMA的阻尼能力。较长时间在650℃退火的样品由于R相形成的减少而具有较低的tanδ值。因此，通过适当地控制冷轧Ti_（50）Ni_（50）的退火条件以产生足够的R相马氏体，可以获得与显着​​的软化储能模量相关的良好的阻尼能力。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号