首页> 外文期刊>Materials Chemistry and Physics >Thermoluminescence for rare-earths doped tellurite glasses
【24h】

Thermoluminescence for rare-earths doped tellurite glasses

机译：稀土掺杂碲酸盐玻璃的热致发光

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Thermoluminescence (TL) of TeO_2 glasses doped with 0.001 wt.% of different rare-earth oxides of the type, La_2O_3, CeO_2, Sm_2O_3, Nd_2O_3, Dy_2O_3, and Yb_2O_3 are measured. All glasses are prepared and irradiated under the same conditions. At all γ-dose levels, the peaks of their glow curves occur in 451-508 K. The intensities of the peaks are nearly linear in the dose range of 0.1-10 Gy. In terms of the TL response measured as a function of time, the traps causing the TL glow peaks are stable showing a fading less than 5% for a period of 1 month and become about 15% in 2 months. The activation energy of trap depth is calculated by different methods. Finally, two emission models of the TL phenomena for the present glasses are proposed.
机译：测量了掺有0.001 wt。％不同类型的稀土氧化物La_2O_3，CeO_2，Sm_2O_3，Nd_2O_3，Dy_2O_3和Yb_2O_3的TeO_2玻璃的热致发光（TL）。所有玻璃均在相同条件下准备和辐照。在所有γ剂量水平下，其辉光曲线的峰值出现在451-508K。在0.1-10 Gy的剂量范围内，峰值的强度几乎呈线性。就作为时间函数的TL响应而言，导致TL发光峰的陷阱稳定，在1个月的时间内衰减小于5％，并在2个月内变为约15％。陷阱深度的激活能通过不同的方法来计算。最后，提出了用于本眼镜的TL现象的两个发射模型。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号