机译:Ti-5Al-5Mo-5V-1Cr-1Fe合金高温变形本构模型的建立和动态软化机理的确定
School of Materials Science and Engineering Northwestern Polytechnical University, 127 Youyixi Street, Xi'an 710012, PR China;
School of Materials Science and Engineering Northwestern Polytechnical University, 127 Youyixi Street, Xi'an 710012, PR China;
School of Materials Science and Engineering Northwestern Polytechnical University, 127 Youyixi Street, Xi'an 710012, PR China;
School of Materials Science and Engineering Northwestern Polytechnical University, 127 Youyixi Street, Xi'an 710012, PR China;
School of Materials Science and Engineering Northwestern Polytechnical University, 127 Youyixi Street, Xi'an 710012, PR China;
School of Materials Science and Engineering Northwestern Polytechnical University, 127 Youyixi Street, Xi'an 710012, PR China;
Constitutive model; Dynamic softening mechanism; High-temperature deformation; Dislocation evolution; Titanium alloys;
机译:Nb稳定的超纯17%Cr铁素体不锈钢热变形过程中的本构模型和动态软化机理
机译:基于热活化的AZ31B镁合金高温动态变形本构模型
机译:Ti-6A1-4V和Ti-6.85Al-1.6V合金高温变形机理的本构分析
机译:变形机制对金属和合金力学行为的影响:实验,本构型建模和验证
机译:β-锆合金的高温变形和流动软化。
机译:Al-Zn-Mg-Cu合金热压变形过程中的组织演变及动态软化机理
机译:阿列尼斯和约翰逊烹饪组成型模型对Ti2AlnB基合金高温变形的比较研究
机译:细晶粒和粗粒两相钛合金高温变形行为的本构分析。