首页> 外文期刊>Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing >Effect of minor niobium addition on microstructure of a nickel-base directionally solidified superalloy
【24h】

Effect of minor niobium addition on microstructure of a nickel-base directionally solidified superalloy

机译：微量铌对镍基定向凝固高温合金组织的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron probe microanalysis (EPMA) and differential scanning calorimetry (DSC) were used to study the effect of minor niobium addition on as-cast microstructure of a nickel-base directionally solidified superalloy. A proper niobium addition resulted in the formation of homogeneous γ' particles almost with the same size throughout the whole dendrite. The ternary eutectic reaction L → (M_(23)C_6 + γ + γ) occurred with increasing niobium content, but no eutectic was found when niobium content was high enough because the NbC preferably precipitated and the eutectic reaction was suppressed.
机译：用扫描电子显微镜（SEM），透射电子显微镜（TEM），电子探针显微分析（EPMA）和差示扫描量热法（DSC）研究了少量铌对镍基定向凝固超合金铸态组织的影响。 。适当添加铌会导致形成均匀的γ'颗粒，在整个枝晶中其大小几乎相同。三价共晶反应L→（M_（23）C_6 +γ+γ）随着铌含量的增加而发生，但是当铌含量足够高时，由于NbC最好析出并抑制了共晶反应，所以没有发现共晶。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号