机译:宏观调度诱导界面结构及其对镍基合金与10%Cr马氏体钢不同金属焊缝蠕变失效的影响
Department of Mechanical Engineering Tsinghua University Beijing 100084 China Key Laboratory for Advanced Materiak Processing Technology Ministry of Education Beijing 100084 China;
Department of Mechanical Engineering Tsinghua University Beijing 100084 China Key Laboratory for Advanced Materiak Processing Technology Ministry of Education Beijing 100084 China State Key Laboratory of Tribology Tsinghua University Beijing 100084 China Collaborative Innovation Center of Advanced Nuclear Energy Technology Tsinghua University Beijing 100084 China;
Department of Mechanical Engineering Tsinghua University Beijing 100084 China Key Laboratory for Advanced Materiak Processing Technology Ministry of Education Beijing 100084 China;
Shanghai Turbine Plant of Shanghai Electric Power Generation Equipment Co. Ltd Shanghai 200240 China;
Shanghai Turbine Plant of Shanghai Electric Power Generation Equipment Co. Ltd Shanghai 200240 China;
Department of Mechanical Engineering Tsinghua University Beijing 100084 China Key Laboratory for Advanced Materiak Processing Technology Ministry of Education Beijing 100084 China;
Department of Mechanical Engineering Tsinghua University Beijing 100084 China Key Laboratory for Advanced Materiak Processing Technology Ministry of Education Beijing 100084 China;
Dissimilar metal weld; Macrosegregation; Interface structure; Phase transformation; Creep failure;
机译:镍基焊接金属异种T91 / TP316H马氏体/奥氏体焊接接头的组织和蠕变特性
机译:镍基填料金属类型对617B和10%Cr马氏体钢的不同金属焊缝蠕变性能的影响
机译:SAF 2507不锈钢与Incoloy 825 Ni基合金之间的异种焊接:微观结构对焊接金属腐蚀行为的作用
机译:铸造不锈钢中镍合金与疲劳裂纹的不同金属焊缝裂纹表面谐波成像
机译:电弧焊焊缝中的宏观偏析是由不同的填充金属引起的。
机译:MIG法焊接铝合金与钢的金属间层的显微组织研究
机译:马氏体和先进的奥氏体高温蠕变抗钢材不同的金属焊缝:蠕变破裂测试结果和融合线调查