首页> 外文期刊>Materials Science and Engineering >Single Crystal Zno: Al Nanoparticles Directly Synthesized Using Low-pressure Spray Pyrolysis
【24h】

Single Crystal Zno: Al Nanoparticles Directly Synthesized Using Low-pressure Spray Pyrolysis

机译：单晶Zno：使用低压喷雾热解法直接合成Al纳米颗粒

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Aluminum-doped zinc oxide (AZO) nanoparticles powder were prepared using low-pressure spray pyrolysis (LPSP). AZO nanoparticles sized 16 and 20 nm with nearly spherical shapes and a crystal size of 11 and 15 nm were yielded using zinc acetate precursor at a low-pressure of 8.0 kPa with a pyrolysis temperature of 800 and 1000℃. The thin films were deposited using a dip-coating method derived from the as-prepared AZO nanoparticles. The thin films that were heated for 1.5 h showed a transmittance higher than 97% in the wavelength range of 400-800 nm and a resistivity of 4.0 × 103 ohm cm with a film thickness of 250 nm. The high crystallinity and high transmittance of AZO nanoparticles that are directly synthesized using the LPSP process have potential for applications as transparent conducting material.
机译：使用低压喷雾热解法（LPSP）制备了铝掺杂的氧化锌（AZO）纳米颗粒粉末。使用乙酸锌前驱体，在8.0 kPa的低压下，在800和1000℃的热解温度下，制得尺寸为16和20 nm的具有近球形的AZO纳米颗粒，晶体尺寸分别为11和15 nm。使用从制备的AZO纳米颗粒衍生的浸涂方法沉积薄膜。加热1.5 h的薄膜在400-800 nm的波长范围内显示出高于97％的透射率，并且在250 nm的膜厚下具有4.0×103 ohm cm的电阻率。使用LPSP工艺直接合成的AZO纳米颗粒的高结晶度和高透射率具有作为透明导电材料应用的潜力。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号