首页> 外文期刊>Materials Science and Engineering. B, Solid-State Materials for Advanced Technology >Photoluminescence properties of Er~(3+)-doped Ba_(0.5)Sr_(0.5)TiO_3 prepared by sol-gel synthesis
【24h】

Photoluminescence properties of Er~(3+)-doped Ba_(0.5)Sr_(0.5)TiO_3 prepared by sol-gel synthesis

机译：溶胶-凝胶法制备掺Er〜（3+）的Ba_（0.5）Sr_（0.5）TiO_3的光致发光性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Er~(3+)-doped Ba_(0.5)Sr_(0.5)TiO_3 (BST) powders were prepared by using barium nitrate, strontium nitrate, tetrabutyl titanate, and ammonia via citrate-nitrate combustion process, along with the XRD, DSC/TGA, and SEM analytic reports. The Er~(3+) luminescence intensity reached a maximum value in the sample with 3 mol% Er~(3+) ions concentration sintered at temperature 1300℃. We also showed that 1 mol% Er dopant improved the dielectric property of BST and the BST:Er materials may have potential use for electroluminescence devices.
机译：硝酸钡，硝酸锶，钛酸四丁酯和氨水通过硝酸硝酸盐燃烧工艺，X射线衍射，DSC / X射线衍射法制备了掺Er〜（3+）的Ba_（0.5）Sr_（0.5）TiO_3（BST）粉末。 TGA和SEM分析报告。在1300℃的温度下烧结3mol％的Er〜（3+）离子，样品中的Er〜（3+）发光强度达到最大值。我们还表明，1摩尔％的Er掺杂剂可改善BST的介电性能，并且BST：Er材料可能具有电致发光器件的潜在用途。