摘要

This research studies the properties of a plain knitted fabric made from cotton/T-400 ring core spun yarn and 100% cotton ring spun yarn. Properties of plain knitted fabric made from 100% cotton ring spun yarn were compared with one made from cotton/T-400 (70.4C/29.6T). We focused on knitted fabric properties such as the bursting strength, elongation at break, tensile strength, air permeability as well as pilling properties. The two yarn samples were produced on the ring frame which had a special attachment for core spun yarn. Fabrics were then knitted using a circular machine, for consistence of results plain knit structure was adopted for all samples. Knitted fabric properties were then tested and results statistically analyzed. Research results show that, plain knitted fabrics made from cotton/T-400 (70.4C/ 29.6T) ring core spun yarn exhibit better elongation at break, bursting strength and air permeability. Whereas the fabric made from 100% cotton showed better pilling resistance and tensile strength compared to cotton/T-400 (70.4C/29.6T) plain knitted fabric. Results show that T-400 filament has very significant influence on resulting fabric properties and hence can be technically manipulated to suit different fabric end use requirements.
机译：本研究研究了由棉/ T-400环芯短纤纱和100％棉环短纤纱制成的平纹针织物的性能。将由100％棉环锭细纱制成的平纹针织物与由棉/ T-400（70.4C / 29.6T）制成的平纹针织物的性能进行比较。我们专注于针织物的性能，例如断裂强度，断裂伸长率，拉伸强度，透气性以及起球性。两种纱线样品均在具有专用于包芯纱的环架上生产。然后使用圆机针织织物，以确保结果一致，所有样品均采用平针织结构。然后测试针织物的性能，并对结果进行统计分析。研究结果表明，由棉/ T-400（70.4C / 29.6T）环芯短纤制成的平纹针织物表现出更好的断裂伸长率，破裂强度和透气性。与棉/ T-400（70.4C / 29.6T）平纹针织面料相比，由100％棉制成的织物显示出更好的抗起球性和拉伸强度。结果表明，T-400长丝对最终的织物性能有非常重要的影响，因此可以在技术上进行操作以适应不同的织物最终用途要求。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号